Continuous carbon fiber reinforced implant-grade PEEK material: AKSOPEEK®LCF is a composite material formed by combining AKSOPEEK® material with continuous carbon fiber. It has excellent fatigue resistance and mechanical strength, can extend service life, is radiolucent, and does not affect the observation of postoperative surgical site healing.
Property Table
| performance | Reference Standard | unit | Actual measurement results |
| performance | Reference Standard | unit | Actual measurement results |
| carbon fiber mass content | ASTM D3529 | % | 66 |
| density | ASTM D792 | g/cm³ | 1.58 |
| hardness | ASTM D785 | / | 104 |
| Tensile strength | ASTM D3039 | MPa | 880 |
| Tensile modulus | ASTM D3039 | GPa | 73 |
| Bending strength | ASTM D7264 | MPa | 1400 |
| Flexural modulus | ASTM D7264 | GPa | 65 |
| Compressive strength | ASTMD 6641 | MPa | 670 |
| compression modulus | ASTMD 6641 | GPa | 60 |
| Heat distortion temperature | ASTM D648 | ℃ | 332 |
| Post-impact compressive strength | ASTM D7137 | MPa | 225 |
| Type I interlaminar fracture toughness | ASTM D5528 | J/m² | 1410 |
| Short beam strength | ASTM D2344 | MPa | 100 |
| In-plane shear strength -0.5% | ASTM D3518 | MPa | 130 |
| In-plane shear modulus | ASTM D3518 | GPa | 5.2 |
1. Typical values are for injection molding indicators.
If needed, please call our technical department to request more detailed technical specifications!
2. This performance indicator cannot be used as a material acceptance standard.